Sliding metals show fluidlike behavior, new clues to wear

ScienceDaily (Sep. 11, 2012) ? Researchers have discovered a swirling, fluid-like behavior in a solid piece of metal sliding over another, providing new insights into the mechanisms of wear and generation of machined surfaces that could help improve the durability of metal parts.

Studies using a microscope and high-speed camera revealed the formation of bumps, folds, vortexlike features and cracks on the metal surface. The findings were surprising because the experiment was conducted at room temperature and the sliding conditions did not generate enough heat to soften the metal.

"We see phenomena normally associated with fluids, not solids," said Srinivasan Chandrasekar, a Purdue University professor of industrial engineering who is working with postdoctoral research associates Narayan Sundaram and Yang Guo.

Numerous mechanical parts, from bearings to engine pistons, undergo such sliding.

"It has been known that little pieces of metal peel off from sliding surfaces," Chandrasekar said. "The conventional view is that this requires many cycles of rubbing, but what we are saying is that when you have surface folding you don't need too many cycles for these cracks to form. This can happen very quickly, accelerating wear."

Findings are detailed in a research paper published in the Sept. 7 issue of Physical Review Letters. The magazine featured the research on the cover and also included a Viewpoint commentary about the work.

The researchers are developing models to further study the phenomena and understand the wide-ranging consequences of such fluid-like flow in metals, Chandrasekar said. The findings might also lead to improved surface quality in materials processing.

The team observed what happens when a wedge-shaped piece of steel slides over a flat piece of copper. It was the first time researchers had directly imaged how sliding metals behave on the scale of 100 microns to 1 millimeter, known as the mesoscale.

The observations show how tiny bumps form in front of the steel piece, followed by the swirling vortexlike movement and then the creation of shallow cracks. The folding and cracking were most pronounced when the steel piece was held at a sharp angle to the copper surface.

The researchers hypothesize that the folding and cracking are due in part to a phenomenon similar to "necking," which happens as a piece of metal is stretched.

Researchers used a specialized laboratory setup that included a high-speed camera and equipment that applies force to the sliding metals. The behavior was captured in movies that show the flow in color-coded layers just below the surface of the copper specimen. Copper is commonly used to model the mechanical behavior of metals.

"Researchers have never had a good experimental setup to observe this kind of deformation directly," Guo said. "Our setup enables us to see the entire history of this fluid-like behavior as it occurs, whereas more conventional experiments rely on still images taken after the experiment is finished."

Metals are made of groups of crystals called grains. Metal surfaces that have smaller grains may be less susceptible to the folding and crack formation.

"We need to explore what role grain size plays," Chandrasekar said. "We think there should be some grain size below which this folding mechanism might be less active. We need to explore why -- under what conditions -- solid metals behave like fluids."

The research has been funded by the National Science Foundation, U.S. Army and General Motors.

Share this story on Facebook, Twitter, and Google:

Other social bookmarking and sharing tools:


Story Source:

The above story is reprinted from materials provided by Purdue University. The original article was written by Emil Venere.

Note: Materials may be edited for content and length. For further information, please contact the source cited above.


Journal Reference:

  1. Narayan Sundaram, Yang Guo, Srinivasan Chandrasekar. Mesoscale Folding, Instability, and Disruption of Laminar Flow in Metal Surfaces. Physical Review Letters, 2012; 109 (10) DOI: 10.1103/PhysRevLett.109.106001

Note: If no author is given, the source is cited instead.

Disclaimer: Views expressed in this article do not necessarily reflect those of ScienceDaily or its staff.

Source: http://feeds.sciencedaily.com/~r/sciencedaily/~3/zRk06YSu5JE/120911151945.htm

leah remini desean jackson kyle orton kyle orton ncaa tournament schedule black and tan dwight howard trade

No comments:

Post a Comment

Note: Only a member of this blog may post a comment.